钢筋混凝土结构抵抗氯盐或硫酸盐侵蚀的成套防治技术

时间:2022-03-17 09:37:03 公文范文 来源:网友投稿

  摘要:为了提升钢筋混凝土结构在氯盐或硫酸盐环境中的服役寿命,本文提出了“隔、阻、缓”一整套耐久性提升技术:发明有机外防水技术与无机渗透强化技术,“隔”离海水的侵蚀;发明混凝土高效盐结晶抑制技术和侵蚀性离子传输抑制技术,大幅降低SO42- 对混凝土的腐蚀和Cl-的传输“阻”止有害离子的侵蚀;发明钢筋长效阻锈技术,延“缓”钢筋锈蚀。
  Abstract: In order to enhance the service life of reinforced concrete structures in the environment of chloride salt or sulphate, this paper proposes a set of durability improvement technologies for "separation, resistance, and retardation": the invention of organic external waterproof technology and inorganic osmotic strengthening technology to separate erosion from seawater; invention of concrete high-stable salt crystallization suppression technology and aggressive ion transmission suppression technology, which significantly reduce the corrosion of SO42- to concrete and Cl-transport, to resist harmful ion erosion; invention of steel long-term rust-proof technology, to retard rebar corrosion.
  关键词:钢筋混凝土;氯盐环境;耐久性;“隔、阻、缓”
  Key words: reinforced concrete;chlorine salt environment;durability;"separation, resistance, retardation"
  中圖分类号:TU375 文献标识码:A 文章编号:1006-4311(2018)14-0121-04

0 引言


  随着海洋及西部大开发战略正逐步实施,钢筋混凝土结构所面临的服役环境愈加严苛,主要体现在服役环境中的侵蚀离子(Cl-、SO42-)浓度愈来愈高,严重威胁着钢筋混凝土结构的服役寿命。这些严酷的环境主要集中在海洋地区以及西部盐湖地区。我国幅员辽阔,海洋面积达299.7万平方公里,占总面积的31%;另外我国大西北有4大盐湖区共上千个盐湖,其中,新疆盐湖区有102个,青海盐湖区有33个,内蒙古盐湖区有370多个,西藏盐湖区有220 多个;盐湖卤水的含盐量高达海水含盐量的5倍~10倍,具体如表1所示,而且主要是以硫酸盐、氯盐为主,对混凝土和钢筋混凝土结构的耐久性构成严重威胁,是造成结构工程过早失效的主要原因。例如:拆除中的青岛北海船厂修船码-服役寿命不到32年,青岛海港站挡浪坝工程位于小麦岛,服役寿命仅有23年;OPC在盐湖卤水干湿交替条件下,2~3年即发生严重腐蚀,破坏位置主要在地面上30cm区域。;ۯ][V-pjx	!ىh-t +ɠ㐚 5j总结两方面的影响,碳化会使氯离子固化能力下降;王绍东指出碳化能够使Cl-型AFm转化为CO32-型AFm,释放出氯离子,加速侵蚀过程。电场条件下比自然状态下氯离子的结合能力要低,影响大小主要依据于电场强度的大小。